Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 14, Article number: 1928 (2024 ) Cite this article 550w Solar Module
High-quality epitaxial p-type V2O3 thin films have been synthesized by spray pyrolysis. The films exhibited excellent electrical performance, with measurable mobility and high carrier concentration. The conductivity of the films varied between 115 and 1079 Scm−1 while the optical transparency of the films ranged from 32 to 65% in the visible region. The observed limitations in thinner films’ mobility were attributed to the nanosized granular structure and the presence of two preferred growth orientations. The 60 nm thick V2O3 film demonstrated a highly competitive transparency-conductivity figure of merit compared to the state-of-the-art.
Yusaku Magari, Taiki Kataoka, … Mamoru Furuta
Xitao Guo, Yonghao Tan, … Jijun Zou
Merlin von Soosten, Dennis.V. Christensen, … Nini Pryds
P-type Transparent Conductive Oxides (TCOs) possess wide-ranging potential in various technological applications, including solar cells1, organic light-emitting diodes2, transparent thin-film transistors3, and more4. However, current p-type TCOs do not exhibit the necessary combination of electrical conductivity and transparency required for widespread industrial use, unlike their n-type counterparts4,5,6,7. To meet the demands of photovoltaics and water-splitting technologies, there is a crucial need for high-performance p-type TCOs capable of facilitating effective hole collection and enabling the fabrication of efficient transparent p-n junctions8,9. As a result, the development of a high figure of merit p-type TCO has become an urgent issue and a subject of intense research4,6,10.
In a recent study by Hu et al.11, it was demonstrated that pulsed laser deposited (PLD) grown V2O3 has the potential to serve as a new p-type TCO. V2O3 exhibits electron correlation due to the on-site Coulomb interaction, leading to changes in the valence band that promote p-type conductivity. Furthermore, the screened plasma energy in V2O3 is positioned below the visible region, resulting in enhanced optical transparency. At room temperature, V2O3 adopts a corundum structure with a space group of \(R\overline{3 }c\) and lattice parameters of a = 4.942 Å and c = 13.99 Å12 (Fig. 1a). This material undergoes a Metal–Insulator Transition (MIT) at low temperatures (~ 150 K)13, where the corundum structure with metallic conductivity transforms into an insulating monoclinic structure with a space group of \(C2/c\) 14. The lattice parameters in the monoclinic phase are a = 8.60 Å, b = 5.00 Å, c = 5.55 Å, and β = 123.1°. In V2O3, the 3d bands split into twofold eg and threefold t2g bands. The t2g bands further degenerate into low-lying doubly degenerate eπg and nondegenerate a1g bands due to the trigonal distortion of the rhombohedral lattice (Fig. 1b). In the metallic phase of V2O3, the valence band (VB) is composed of eπg and a1g bands, and it is partially occupied by two t2g electrons (Fig. 1c). The Fermi level is within the upper VB, explaining the p-type conduction of V2O3 with high conductivity (σ) and hole concentration (nh). Unlike most p-type TCOs, this characteristic of V2O3 allows for circumventing issues associated with hole doping, such as the high formation energy of native acceptors and self-compensation effects10,11,15.
V2O3 crystal structure (a) above the MIT temperature (~ 150 K), (b) the simplified V2O3 t2g band diagram and (c) a sketch of VB modification due to electron correlation in V2O3 (UHB, LHB are the upper and the lower Hubbard band, respectively).
The renormalization factor Zk, defined as the ratio of the free non-interacting electron effective mass (mband) to the renormalized electron effective mass (m∗ ) that incorporates electron–electron interaction, can be used to quantify the strength of electron correlation. In the case of V2O3, Zk is equal to 0.1211. The hole effective mass in V2O3 is larger than that in conventional TCO materials and can be estimated as m* = mband/Zk ≈ 8.3mband. This increase of the effective mass occurs due to the localization of vanadium 3d electron orbitals near the VB maximum. Although a large hole effective mass typically hampers hole mobility, the high hole concentration (nh) compensates for it, resulting in high conductivity for V2O310,11,15. To achieve optical transparency in the visible range, the reflection edge in the material should be below 1.75 eV, while the strong interband optical transition should be above 3.25 eV. The screened plasma energy ħωp, which describes the free carrier reflection edge, can be calculated as ħωp = (e2/ε0εr)1/2(n/m∗ )1/2, where n is the carrier concentration, e is the elemental charge, ε0 is the vacuum permittivity, and εr is the relative permittivity. The enhanced m* = 8.3mband in V2O3, resulting from electron correlation, tunes the n/m∗ ratio in such a way that ħωp shifts below 1.75 eV, enabling optical transparency of V2O3 in the visible range. Additionally, the optical absorption in the visible region of V2O3 is governed by the d-d transition from occupied t2g to empty t2g bands, which are low, allowing V2O3 films to remain sufficiently transparent. The upper limit of transparency (EH), where strong absorption is observed at a photon energy around 4 eV, is controlled by charge transfer excitations from O2p to t2g bands in the ultraviolet region10,11,15.
Limited research has been conducted on the deposition of p-type V2O3 utilizing simpler growth techniques than various physical vapour deposition (PVD) methods. Consequently, there is a need to explore alternative fabrication approaches offering the synthesis of the high-quality p-type V2O3. In this study, we present, to our knowledge, the successful synthesis of high-quality p-type V2O3 TCO thin films on c-plane Al2O3 substrate using a single-step spray pyrolysis (SP) method. The structural, optical, and electrical properties of V2O3 of various thicknesses were characterized in relation to TCO application. The deposited p-type V2O3 films exhibited an epitaxial structure with the substrate and a conductivity of 1079 Scm−1 (0.05 M, 60 nm thick sample), which is the highest reported for a solution-based thin film growth method to date, without requiring post-deposition treatment. Furthermore, the grown V2O3 samples demonstrated quantifiable mobility through simple dc Hall measurements and exhibited relative atmospheric stability. Although the Figure of Merit (FoM) by Gordon and Haacke of the SP-grown V2O3 thin film (0.05 M, 60 nm thick sample) was smaller compared to their PLD-grown counterparts11, the obtained FoM is the highest reported for SP-grown p-type TCOs and surpasses several other PVD-grown p-type TCOs. We attribute the primary limiting factor in electrical performance to film morphology and growth orientation, which can be linked to inherent factors in our deposition setup. Nevertheless, the low-cost, non-vacuum, and high-yield spray pyrolysis method16,17 stands out as a simple, scalable, and cost-effective approach for fabricating p-type V2O3, which is important considering the potential applicability of p-type V2O3 in device applications such as rectifiers, photodetectors, and solar cells.
The details of the chamber geometry, nozzle type, and other parameters, experimental details of this study are provided elsewhere18. In summary, all thin films were deposited on single-side polished c-Al2O3 substrates (10 × 10 mm, 1 mm thick). The precursor used was vanadium (III) acetylacetonate V(C5H7O2)3 (Sigma Aldrich), which was dissolved in methanol at varying (0.05, 0.025, 0.015, 0.10, and 0.005 M) molarities (concentrations) to achieve different film thicknesses. The thickness of the sample grown with a solution molarity of 0.05 M was determined to be 60 nm using ellipsometry, which will be discussed in detail later. Under the assumption that the grown film thickness is proportional to molarity19, the thicknesses of the remaining samples are estimated to be: 0.025 M—30 nm; 0.015 M—20 nm; 0.01 M—15 nm; 0.005 M—10 nm. To ensure clarity throughout the text, the thicknesses will be explicitly referenced and utilized. It should be noted that vanadium (III) acetylacetonate exhibits high solubility in methanol without any observable precipitation. The solution was sprayed onto a heated substrate at a heater temperature of 718 ± 5 K using compressed nitrogen gas with a flow rate of 15 L/min. The heater temperature was controlled using a PID controller, and a type K thermocouple attached to the heater surface provided temperature feedback.
To analyze the out-of-plane orientations of the films, as well as the in-plane orientation for determining the epitaxial relationship between the film and substrate, symmetric θ/2θ-scans and φ-scans were performed using a Bruker D8 Advance X-ray diffraction (XRD) system with a Cu Kα source. The XRD system was equipped with a Ge (002) double bounce monochromator. Additionally, Raman measurements were conducted at room temperature using a Witec Alpha 300R instrument with an excitation wavelength of 532 nm and a power level below 1 mW to prevent local heating effects. Surface morphology and roughness were investigated using Bruker atomic force microscopy (AFM) in tapping mode with a probe tip diameter of 20 nm. Optical properties were characterized using UV–VIS spectrometer (PerkinElmer 650S) and ellipsometry (SOPRA GESP5). For electrical characterization at room and low temperatures, a custom-built four-point probe station with a square Van-der-Pauw geometry and silver paint-based contacts was used. The dc Hall measurements were performed with a maximum magnetic field of 800 mT. All electrical measurements were carried out using a Keithley 2400 source meter.
Figure 2a shows the out-of-plane XRD pattern of the 60 nm (0.05 M) V2O3 sample grown on c-Al2O3 substrate. For this sample, only (000n) order peaks for the V2O3 thin film and Al2O3 substrate are observed, confirming a single crystalline phase and c-axis oriented growth of V2O3. The high quality of the 60 nm (0.05 M) V2O3 sample is further validated through rocking curve measurements (ω scan), revealing a full width at half maximum around 0.05° (Fig. 1b). To determine the epitaxial relationship between film and substrate, φ scans of the V2O3 film (0110) reflection and of the substrate (0110) reflection were performed (Fig. 2c). Since Al2O3 is rhombohedral, the (0110) reflection shows three-fold symmetry. The presence of six peaks for the (0110) reflection of V2O3 instead of expected three implies the presence of the two domains of V2O3. The equal intensity of each of the six observed peaks indicates that each of the two domains are present in approximately equal quantities. The schematics of the two V2O3 domain arrangements on c-Al2O3 is shown in Fig. 3. One of the V2O3 domain’s basal plane is aligned with that of c-Al2O3, whereas for the other domain there is (60°) 180° in-plane rotation. The following epitaxial relation was derived: V2O3 \((0\; 0\; 1)\) ‖ Al2O3 \((0\; 0\; 1)\) ; V2O3 \([2\;\overline{1 }\;\overline{1 }\;0]\) ‖ Al2O3 \([2\;\overline{1 }\;\overline{1 }\;0]\) or V2O3 \([2\;\overline{1 }\;\overline{1 }\;0]\) ‖ Al2O3 \([1\;1\;\overline{2 }\;0]\) .
(a) Full range XRD θ/2θ scan of 60 nm (0.05 M) V2O3 (0001) thin film. (b) XRD rocking curve measurement for the 60 nm (0.05 M) V2O3 (0001) thin film. (c) XRD φ-scan measurements for the 60 nm (0.05 M) V2O3 (0110) planes and Al2O3 (0110) planes. Narrow (d) XRD and (e) Raman scans with data for all samples have been stacked according to the thickness. Shaded area denotes c-Al2O3 (0006) XRD peak.
Schematic showing the alignment of two different domains of V2O3 on the Al2O3.
However, altering the molarity, and consequently, the thickness, of the samples leads to changes in the observed reflexes of the V2O3 thin films (Fig. 2d). When the thickness is less than 30 nm (0.025 M) the (110) reflection is present in addition to the (0006) reflection. The intensity of the XRD reflections reduces gradually with decreasing thickness because the scattered intensity is proportional to the sample thickness. The peak broadening without a shift in position is also observed as thickness is reduced, due to a thickness decrease from 60 to 5 nm. We propose that an increased thickness leads to the formation of an epitaxial thin film. However, the appearance of an additional peak to (001), such as the (110) below a thickness of 30 nm, suggests a deviation from epitaxial growth at smaller thicknesses. To the best of our knowledge, the occurrence of V2O3 (110) orientation on c-Al2O3 has not been observed through physical vapor deposition (PVD) methods20,21. Nevertheless, in a study22 it was reported the presence of the (110) peak in the XRD pattern of V2O3 grown using a sol–gel method on c-Al2O3. It seems that, particularly in V2O3 prepared from a solution, there is a competition in preferential growth orientations between (110) and (001) planes. In our experiments involving samples of varying thickness, a consistent trend emerged. Larger thicknesses seemed to promote the exclusive growth of the (001) orientation, whereas thinner films exhibited the appearance of the (110) peak in addition to the (006) peak. Understanding such changes requires additional measurements, as they could occur due to various factors, such as strain relaxation or surface energy minimization. Typically the thin film texture for SP grown films strongly depends on substrate, solvent and precursor choice18, but in the case of strongly textured growth an influence on growth rate (affected by molarity) is also frequently observed23. The biaxial in-plane strain values for (110) on c-Al2O3 are 4.1% and 1.94%, whereas for (001), they are both 4.1%. In this context, there is a comparable likelihood of initiating either (110) or (001) growth orientations. The growth rate is a key factor influencing the dynamics of surface diffusion, which involves the movement of adatoms across the substrate surface. Specifically, for (110) growth orientation, adatoms need to traverse a larger distance across the substrate surface. There is a possibility that a slower growth rate might promote (110) growth orientation because adatoms would have ample time for lateral diffusion before being incorporated into the film. Conversely, higher growth rates could limit the time available for lateral diffusion, resulting in the incorporation of adatoms into the film and promoting (001) orientation. Deposition techniques that introduce a higher flux of adatoms to the substrate surface, such as sputtering or molecular beam epitaxy, generally yield higher growth rates compared to other methods, thereby probably favouring the growth of (001) orientation. For solution-based thin film growth techniques like spray pyrolysis, the growth rate is partially controlled by the concentration of the precursor in the solvent. Lower concentrations encourage a slower growth rate, enabling the fabrication of thinner films with the presence of (110) growth orientation. The question of why (110) growth orientation persists to substantial thicknesses in V2O3 obtained by a solution-based process is one that we plan to address in future research.
Additionally, Raman spectroscopy was performed to confirm the phase identification of the V2O3 samples (Fig. 2e). V2O3 has 7 Raman-active modes (2A1g + 5Eg) for a crystal with a corundum structure24. First A1g mode is experimentally observed at 240 cm−1 and it is related to the vibration of the vanadium atoms along the z-axis towards the oxygen triangle plane and back. While the second A1g mode observed at 510 cm−1 belongs to the vibration of the oxygen atoms towards the z-axis and back in the basal plane. The first Eg mode at 218 cm−1 is attributed to the out-of-phase movement of vanadium in the basal plane. In phase motion of vanadium atoms yield the second Eg mode at 300 cm−1. The remaining Eg modes describe the complex motion of oxygen atoms and are found at 340 and 600 cm−1. Another Eg mode at 378 cm−1 was not observed experimentally but it was theoretically predicted24. In our Raman measurements, broad an asymmetric peak covering a range of 160–250 cm−1 is clearly observable, probably due to convolution of the first Eg (218 cm−1) and A1g (240 cm−1) modes. This broad peak is redshifted as thickness decreases, possibly due to strain15. The remaining expected peaks are not that pronounced in intensity or absent, which was observed for V2O3 thin film in another study15. The Raman peak around 418 and 479 cm−1, related to the c-Al2O3 is absent for all films except the thinnest (10 nm), generally indicating that the coverage of the thin films is continuous and dense.
The AFM scans reveal that SP-grown V2O3 films exhibit a nanosized granular structure. Comparing the roughness of the samples, it is evident that the roughness increases as the thickness increases (Fig. 4a). However, attempts to obtain an x-ray reflectivity oscillations signal from any sample for thickness determination were unsuccessful, presumably due to the high surface roughness.
(a) 5 × 5 µm area AFM images of 60 and 10 nm thick SP-grown V2O3 samples and AFM measured RMS roughness of the V2O3 thin films. (b) RHEED patterns of the SP-grown V2O3 60 nm sample (along Al2O3 \([1\;1\;\overline{ 2 }\;0]\) left and Al2O3 \([1\;0\;\overline{1 }\;0]\) right).
Figure 4b shows RHEED images taken along the Al2O3 \([1\;1\;\overline{2 }\;0]\) and Al2O3 \([1\;0\;\overline{1 }\;0]\) high symmetry directions of a 60 nm thick V2O3 sample. RHEED patterns were obtained post-deposition in a UHV chamber with a pressure less than 5 × 10−9 mbar, using an electron beam energy and current of 20 keV and 1.5 A, respectively. The pattern shown in Fig. 4b displays something between a transmission spot pattern and that of modulated streaks, which is characteristic of a film surface consisting of continuous 3-D islands with a rough surface. This correlates well with the roughness and granular morphology of this sample determined via AFM.
Figure 5a, b and c demonstrate that hole concentration, mobility, conductivity and sheet resistance exhibits a strong dependence on the thickness (molarity of the solution). Consistent with previous studies11,15, the SP-grown V2O3 films exhibit p-type conductivity with high hole concentration (1.04 × 1022–2.86 × 1022 cm3) and low mobility (0.07–0.24 cm2/Vs) values. In comparison to PLD-grown p-V2O311, SP grown samples demonstrate somewhat lower values of the hole concentration and mobility, resulting in lower conductivity values ranging from 115 to 1079 Scm−1. Notably, the sample with the largest thickness exhibits a hole concentration of 2.86 × 1022 cm3 and mobility of 0.24 cm2/Vs, values which are similar to the hole concentration (5.28 × 1022 cm3) and mobility (0.24 cm2/Vs) of the PLD-grown sample11. However, as thickness decreases the hole concentration remains in the same order of magnitude as PLD grown samples11, but mobility decreases more rapidly. In general, mobility reduces with decrease in thickness because of the overall increase in scattering centres. In addition to the size effect, the possible reason for more rapid mobility reduction for SP grown V2O3 can be nanosized granular morphology and the appearance of two growth orientations for samples with smaller thicknesses. This is in contrast to the PLD-grown V2O3 samples11, which exhibit a single orientation and very smooth, non-granular morphology across all thicknesses.
Room temperature (a) hole concentration, mobility, and (b) electrical conductivity. (c) Temperature-dependent sheet resistance.
Mobility in a single crystal depends on the orientation; in the case of a polycrystalline sample, it can be affected by grain boundaries between grains at different orientations and texture. In this regard, the presence of (110) growth orientation in addition to (001) growth orientation might adversely affect mobility in case of SP-grown V2O3. Furthermore, the nanosized granular morphology serves as an effective scattering source for hole transport, thereby reducing mobility. This phenomenon was also observed in a previous study17 conducted by the authors, which investigated zinc tin oxide TCO films deposited using the same SP equipment. In that study17, the limited mobility of charge carriers in zinc tin oxide was attributed to the granular nature of the films.
V2O3 is known to undergo a MIT at 150 K. Therefore, low-temperature resistance measurements were conducted for all samples to investigate this behaviour (Fig. 5c). It is observed that all samples exhibit a transition in resistivity, shifting towards a more insulating state at reduced temperature, with a characteristic hysteresis loop indicative of a first-order phase transition at approximately 150 K. It should be noted that the observed MIT in all samples is suppressed, and the magnitude of the transition and its width are smaller than single crystal bulk V2O3. The thinner films, demonstrate a more pronounced MIT compared to the thicker samples. However, the 15 nm thick sample deviates from this pattern. Evidently, this particular sample exhibits a distinct prevalence of (110) crystallographic orientation in comparison to the other samples, which potentially underlies this unique behavior25. It should be noted that a growth orientation of (110) was achieved on the a-Al2O3 substrate in the studies20,21 using PVD techniques, resulting in a pronounced MIT at approximately 150 K. In contrast, our samples deviate from this approach as we employ a solution spraying method, resulting in non-epitaxial V2O3 films with a thickness of 15 nm on c-Al2O3 with two growth orientations, (110) and (001). This difference complicates direct comparisons with the epitaxial films discussed in the aforementioned studies20,21. The presence of internal strain and stress, stemming from crystal orientation mismatches in materials with several growth orientations or texture, has the potential to alter the structure and MIT properties of V2O326,27,28. Shifts in the MIT temperature and stabilization of the metallic phase in thicker films have been observed in PLD-deposited V2O3 films29,30,31. Allimi et al29 suggested that the observed behavior in the thicker films might be related to specific defect microstructures that induce localized conditions analogous to the application of a hydrostatic pressure in bulk. In order to comprehensively elucidate the intricate relationship between resistance variation and temperature in V2O3, further microstructural analysis is required29,30,31.
Given the potential use of the films as TCO their optical properties are also of importance. Figure 6a summarises the transmission measurements for the spray grown V2O3 samples. Room temperature transmission ranges 32–65% for the visible and near-infrared ranges. The transparency of the V2O3 thin films is reduced with increasing film thickness due to the unavoidable optical absorption in the visible region. The behaviour of light passing through a thin film can be understood by considering its complex refractive index32. This index, denoted by ñ, consists of two parts: the real refractive index (n) and the imaginary extinction coefficient (κ). To determine the thickness of the sample grown with a solution molarity of 0.05 M and its complex refractive index, room temperature ellipsometry measurements were performed. The thickness of the sample grown with a solution molarity of 0.05 M was determined to be 60 nm.
(a) UV–Vis transmittance spectra for the Al2O3 substrate and V2O3 thin films with different thicknesses and (b) 60 nm thick (0.05 M) V2O3 film’s refractive index n, and extinction coefficient k, as a function of photon energy in the wide spectral range modelled from the ellipsometry data. The larger step in transmission reduction from the bare Al2O3 to 10 nm V2O3 is caused by the larger refractive index of V2O3 compared to Al2O3 and hence an increased reflection loss.
The transmission of light through a sample depends on its reflectivity and absorption coefficient. Figure 6b illustrates the variation of n and κ for the 60 nm V2O3 thin film as a function of photon energy. The extinction coefficient κ is directly related to the absorption coefficient α of the material, where α = 4πκ/λ and λ is the wavelength of light in vacuum32. A lower value of κ corresponds to lower α, indicating higher transparency. In the visible range (around 2.0 eV), V2O3 exhibits a κ value of approximately 0.4, suggesting good transparency.
However, absorption increases at photon energies above 4.5 eV and in the infrared range below 2 eV due to interband transitions and free carrier excitation, respectively. Determining the bandgap of V2O3 through the absorption coefficient we consider unreliable due to the complex interband states33 in its band structure. Although V2O3 possesses interband states and behaves as a metal at room temperature, it exhibits low absorption below 4.5 eV because of electron correlation effects, which can shift the plasma frequency below 1.75 eV, resulting in optical transparency in the visible range11. Despite being highly conductive, V2O3 thin films have low refractive index values in the infrared and visible spectral regions. This property makes them potentially suitable as buffer layers in organic light-emitting diodes or solar cell devices where a reduced refractive index or lower work function is required for the transparent contact34. For instance, V2O3's refractive index of 1.8 in the visible region is ideal for minimizing reflective losses at glass/TCO interfaces while maintaining conductivity35.
In crystalline materials, the electrical properties can vary significantly between thinner films and films with micrometer thickness, depending on the growth method and conditions. As a result, deriving a representative FoM for the material can be challenging, and it becomes harder to differentiate between systematic issues in the FoM calculation and genuine material changes. This complexity arises due to the differences in grain sizes and associated electrical properties between the two film thickness regimes.
The preferable way of evaluating TCO performance is based on calculation of the FoM by using its conductivity and absorption coefficient FoMTR = σ/α = −1/(Rs ln(T + R))46. For the sample V2O3 with 60 nm thickness this FoM will be 2776.7 µS. This expression provides a measure of the TCO's quality, independent of its thickness, and has units of Siemens. It can be determined by measuring the thin film's sheet resistance (Rs), transmittance (T), and reflectance (R) without requiring detailed knowledge of the film thickness. This makes it an ideal quantity for experimental screening purposes. In epitaxial systems where the TCO's microstructure remains unaffected by the sample thickness, FoMTR serves as a reliable parameter for comparing the performance of p-type TCOs. When using this FoM the challenge arises when UV–VIS spectrometers lacking the capability to perform reflectance measurements is utilized, in this case the FoM is reduced to the −1/Rs ln(T). FoM loses its thickness independence, making it difficult to compare samples with different thicknesses reliably. Moreover, relying solely on transmission data can be problematic since it becomes challenging to distinguish between unwanted absorption losses and acceptable reflection losses. Another concern is that the FoM alone does not provide information about a material's band gap or hole mobility, which are crucial for optoelectronic devices. Therefore, a high FoM does not necessarily translate to enhanced efficacy in a specific device46. To evaluate the performance of SP-grown V2O3 as a p-type TCO, two commonly used FoM were calculated: the Haacke47 FoM (FoMH = T10/Rs) and the Gordon48 FoM (FoMG = −1/(Rs ln T)). The FoM calculations were performed for the sample grown from a 0.05 M solution, which had its thickness (60 nm thick) precisely determined through ellipsometry measurements (in contrast to the estimated thickness of the other samples). Table 1 presents a comparison of the FoM values for various p-type materials, including the 0.05 M 60 nm thick V2O3 sample. Although our SP-grown V2O3 exhibits a smaller FoM compared to the remarkably high FoM of PLD-grown V2O3 samples11,15, it still stands out as being comparable to or even higher than other p-type TCOs obtained through both chemical and physical deposition methods. This demonstrates the capability of the spray pyrolysis technique to produce high-performance p-type TCOs, particularly electron-correlated materials like V2O3. We propose that further improvements in SP-grown V2O3 as a p-type TCO can be achieved by better control over the growth conditions. It is crucial to prevent the presence of multiple growth orientations and strive for a smooth surface with larger grains, as these factors can significantly enhance mobility, hole carrier concentration, and ultimately, conductivity.
In summary, we demonstrated successful growth of epitaxial p-type V2O3 thin films exhibiting excellent electrical performance for films deposited by inexpensive chemical synthesis methods. The highest-performing sample achieved a conductivity of 1079 Scm−1 (0.05 M, 60 nm thick V2O3 sample) obtained in single step without any post-deposition treatment is the highest reported for a solution-based thin film growth method to date. The deposited p-type V2O3 films have measurable mobility (0.07–0.24 cm2/Vs) and high carrier concentration (1.04 × 1022–2.86 × 1022 cm3) with a conductivity that varies between 115–1079 Scm−1. The optical transparency is in the range of 32–65%. The transparency is on the lower side at larger thicknesses and it is improving at small thicknesses. The FoM value of the V2O3 film (0.05 M, 60 nm thick sample) is found to be highly competitive even with several other PVD deposited p-type TCOs despite the constraints arising from the specifics of the utilized deposition system. We suggest that nanosized granular structure along with the presence of more than one preferred growth orientation in particular limits mobility. The more specialized system with a superior nebulizer could help overcome these limitations to push the conductivity and transparency of the SP grown V2O3 towards higher values. In general, the high conductivity and acceptable transparency at low thicknesses make V2O3 quite suitable as an active element facilitating the transport of photogenerated holes in solar cells. Future research should explore the deposition of V2O3 films on non-single crystal and inexpensive substrate such as glass while maintaining similar electrical and optical performance. Furthermore, exploring the physical mechanism responsible for the emergence of (110) growth orientations alongside (001) growth orientation in the grown V2O3 samples presents a very interesting question for future works.
Yusaku Magari, Taiki Kataoka, … Mamoru Furuta
Xitao Guo, Yonghao Tan, … Jijun Zou
Merlin von Soosten, Dennis.V. Christensen, … Nini Pryds
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Yu, W. et al. Performance improvement of inverted polymer solar cells thermally evaporating nickel oxide as an anode buffer layer. Sol. Energy Mater. Sol. Cells 98, 212–215 (2012).
Wang, Y. et al. Ultrathin nickel oxide film as a hole buffer layer to enhance the optoelectronic performance of a polymer light-emitting diode. Opt. Lett. 36, 1521–1523 (2011).
Article ADS CAS PubMed Google Scholar
Kawazoe, H., Yanagi, H., Ueda, K. & Hosono, H. Transparent p-type conducting oxides: Design and fabrication of p-n heterojunctions. MRS Bull. 25, 28–36 (2000).
Wang, Z., Nayak, P. K., Caraveo-Frescas, J. A. & Alshareef, H. N. Recent developments in p-type oxide semiconductor materials and devices. Adv. Mater. 28, 3831–3892 (2016).
Article CAS PubMed Google Scholar
Banerjee, A. N. & Chattopadhyay, K. K. Recent developments in the emerging field of crystalline p-type transparent conducting oxide thin films. Prog. Cryst. Growth Charact. Mater. 50, 52–105 (2005).
Willis, J. & Scanlon, D. O. Latest directions in p-type transparent conductor design. J. Mater. Chem. C 9, 11995–12009 (2021).
Mauit, O. et al. Growth of ZnO: Al by atomic layer deposition: Deconvoluting the contribution of hydrogen interstitials and crystallographic texture on the conductivity. Thin Solid Films 690, 137533 (2019).
Article ADS CAS Google Scholar
Zhang, K. H. L., Xi, K., Blamire, M. G. & Egdell, R. G. P-type transparent conducting oxides. J. Phys. Condens. Matter 28, 383002 (2016).
Farrell, L. et al. Conducting mechanism in the epitaxial $p$-type transparent conducting oxide $\mathrm{C}{\mathrm{r}}_{2}{\mathrm{O}}_{3}:\mathrm{Mg}$. Phys. Rev. B 91, 125202 (2015).
Hu, L. et al. Design strategy for p-type transparent conducting oxides. J. Appl. Phys. 128, 140902 (2020).
Article ADS CAS Google Scholar
Hu, L. et al. Exploring high-performance $p$-type transparent conducting oxides based on electron correlation in ${\mathrm{V}}_{2}{\mathrm{O}}_{3}$ thin films. Phys. Rev. Appl. 12, 44035 (2019).
Andersson, G. Studies on vanadium oxides. I. Phase analysis. Acta Chem. Scand. 8, 1599 (1954).
Morin, F. J. Oxides which show a metal-to-insulator transition at the Neel temperature. Phys. Rev. Lett. 3, 34–36 (1959).
Article ADS CAS Google Scholar
McWhan, D. B. & Remeika, J. P. Metal-insulator transition in (V1-xCrx)(2)O-3. Phys. Rev. B-Solid State 2, 3734–3750 (1970).
Zhu, M. et al. Enhancing the performances of V2O3 thin films as p-type transparent conducting oxides via compressive strain. Appl. Phys. Lett. 121, 61903 (2022).
Crêpellière, J. et al. Spray deposition of silver nanowires on large area substrates for transparent electrodes. ACS Appl. Nano Mater. 4, 1126–1135 (2021).
Zhussupbekova, A. et al. Low-cost, high-performance spray pyrolysis-grown amorphous zinc tin oxide: The challenge of a complex growth process. ACS Appl. Mater. Interfaces 12, 46892–46899 (2020).
Article CAS PubMed Google Scholar
Arca, E., Fleischer, K. & Shvets, I. V. Influence of the precursors and chemical composition of the solution on the properties of ZnO thin films grown by spray pyrolysis. J. Phys. Chem. C 113, 21074–21081 (2009).
Joishy, S. et al. Influence of solution molarity on structure, surface morphology, non-linear optical and electric properties of CdO thin films prepared by spray pyrolysis technique. Mater. Res. Express 6, 106447 (2019).
Article ADS CAS Google Scholar
Kalcheim, Y. et al. Robust coupling between structural and electronic transitions in a Mott material. Phys. Rev. Lett. 122, 57601 (2019).
Article ADS CAS Google Scholar
Zhang, GD et al.Orientation-dependent strain effects on the metal-insulator transitions in $({\mathrm{V}}_{0.99}{\mathrm{Cr}}_{0.01}{)}_{2}{\mathrm{O}} _{3}/{\mathrm{Al}}_{2}{\mathrm{O}}_{3}$ thin films.Phys.Rev.B 105, 35140 (2022).
Chen, X.-B., Kong, M.-H., Choi, J.-Y. & Kim, H.-T. Raman spectroscopy studies of spin-wave in V2O3 thin films. J. Phys. D. Appl. Phys. 49, 465304 (2016).
de Godoy, M. P. F., de Herval, L. K. S., Cotta, A. A. C., Onofre, Y. J. & Macedo, W. A. A. ZnO thin films design: The role of precursor molarity in the spray pyrolysis process. J. Mater. Sci. Mater. Electron. 31, 17269–17280 (2020).
Shvets, P., Dikaya, O., Maksimova, K. & Goikhman, A. A review of Raman spectroscopy of vanadium oxides. J. Raman Spectrosc. 50, 1226–1244 (2019).
Article ADS CAS Google Scholar
Allimi, B. S. et al. Resistivity of V2O3 thin films deposited on a-plane (110) and c-plane (001) sapphire by pulsed laser deposition. Appl. Phys. Lett. 92, 202105 (2008).
Homm, P., Menghini, M., Seo, J. W., Peters, S. & Locquet, J.-P. Room temperature Mott metal–insulator transition in V2O3 compounds induced via strain-engineering. APL Mater. 9, 21116 (2021).
Metcalf, P. A. et al. Electrical, structural, and optical properties of Cr-doped and non-stoichiometric V2O3 thin films. Thin Solid Films 515, 3421–3425 (2007).
Article ADS CAS Google Scholar
Querré, M. et al. Metal–insulator transitions in (V1-xCrx)2O3 thin films deposited by reactive direct current magnetron co-sputtering. Thin Solid Films 617, 56–62 (2016).
Allimi, B. S., Aindow, M. & Alpay, S. P. Thickness dependence of electronic phase transitions in epitaxial V2O3 films on (0001) LiTaO3. Appl. Phys. Lett. 93, 112109 (2008).
Autier-Laurent, S., Mercey, B., Chippaux, D., Limelette, P. & Simon, C. Strain-induced pressure effect in pulsed laser deposited thin films of the strongly correlated oxide ${\mathrm{V}}_{2}{\mathrm{O}}_{3}$. Phys. Rev. B 74, 195109 (2006).
Grygiel, C. et al. Thickness dependence of the electronic properties in V2O3 thin films. Appl. Phys. Lett. 91, 262103 (2007).
Moore, E. A. & Smart, L. E. Optical properties of solids. Solid State Chem. An Introd. 283–314 (2020) https://doi.org/10.1201/b12047-14.
Stewart, M. K. et al. Insulator-to-metal transition and correlated metallic state of V${}_{2}$O${}_{3}$ investigated by optical spectroscopy. Phys. Rev. B 85, 205113 (2012).
Fleischer, K., Arca, E., Smith, C. & Shvets, I. V. Aluminium doped Zn1−xMgxO—A transparent conducting oxide with tunable optical and electrical properties. Appl. Phys. Lett. 101, 121918 (2012).
Fleischer, K., Arca, E. & Shvets, I. V. Improving solar cell efficiency with optically optimised TCO layers. Sol. Energy Mater. Sol. Cells 101, 262–269 (2012).
Crêpellière, J. et al. Transparent conductive CuCrO2 thin films deposited by pulsed injection metal organic chemical vapor deposition: Up-scalable process technology for an improved transparency/conductivity trade-off. J. Mater. Chem. C 4, 4278–4287 (2016).
Lunca Popa, P., Crêpellière, J., Nukala, P., Leturcq, R. & Lenoble, D. Invisible electronics: Metastable Cu-vacancies chain defects for highly conductive p-type transparent oxide. Appl. Mater. Today 9, 184–191 (2017).
Farrell, L. et al. Synthesis of nanocrystalline Cu deficient CuCrO2—A high figure of merit p-type transparent semiconductor. J. Mater. Chem. C 4, 126–134 (2016).
Barnabé, A., Thimont, Y., Lalanne, M., Presmanes, L. & Tailhades, P. p-Type conducting transparent characteristics of delafossite Mg-doped CuCrO2 thin films prepared by RF-sputtering. J. Mater. Chem. C 3, 6012–6024 (2015).
Nagarajan, R., Draeseke, A. D., Sleight, A. W. & Tate, J. p-type conductivity in CuCr1−xMgxO2 films and powders. J. Appl. Phys. 89, 8022–8025 (2001).
Article ADS CAS Google Scholar
Kim, J. et al. Highly conductive and visibly transparent p-type CuCrO2 films by ultrasonic spray pyrolysis. ACS Appl. Mater. Interfaces 14, 11768–11778 (2022).
Article MathSciNet CAS PubMed Google Scholar
Hu, L. et al. La2/3Sr1/3VO3 thin films: A new p-type transparent conducting oxide with very high figure of merit. Adv. Electron. Mater. 4, 1700476 (2018).
Soma, T., Yoshimatsu, K. & Ohtomo, A. p-type transparent superconductivity in a layered oxide. Sci. Adv. 6, eabb8570 (2023).
Fu, G. et al. Enhanced transparent conducting performance of c-axis oriented Ca3Co4O9 thin films. RSC Adv. 5, 26383–26387 (2015).
Article ADS CAS Google Scholar
Wei, R. et al. p-type transparent conductivity in high temperature superconducting Bi-2212 thin films. Appl. Phys. Lett. 112, 251109 (2018).
Fleischer, K., Norton, E., Mullarkey, D., Caffrey, D. & Shvets, I. V. Quantifying the performance of p-type transparent conducting oxides by experimental methods. Materials 10, 1019 (2017).
Article PubMed PubMed Central Google Scholar
Haacke, G. New figure of merit for transparent conductors. J. Appl. Phys. 47, 4086–4089 (2008).
Gordon, R. G. Criteria for choosing transparent conductors. MRS Bull. 25, 52–57 (2000).
This work was supported by Irish Research Council (IRC) Laureate Award (IRCLA/2019/171). A.A. gratefully acknowledges financial support of Nazarbayev University under the Talap program and Government of Ireland Postgraduate Scholarship under grant GOIPG/2021/933 IRC. D.C. acknowledges support from the IRC under Grant No. EPSPG/2017/329. A.M. acknowledges support from the IRC under Grant No. GOIPG/2020/621.
School of Physics, Trinity College Dublin, College Green, Dublin 2, Dublin, D02 PN40, Ireland
Ardak Ainabayev, Brian Walls, Daragh Mullarkey, David Caffrey, Christopher M. Smith, Amy McGlinchey, Daniel Casey & Igor Shvets
Centre for Research On Adaptive Nanostructures and Nanodevices, Trinity College Dublin, 43 Pearse St, Dublin 2, Dublin, D02 W085, Ireland
Ardak Ainabayev, Brian Walls, Daragh Mullarkey, David Caffrey, Christopher M. Smith, Amy McGlinchey, Daniel Casey & Igor Shvets
Nazarbayev University, Kabanbay Batyr Ave 53, Astana, 010000, Kazakhstan
Advanced Processing Technology Research Centre, Dublin City University, Glasnevin, Dublin, D09 K2WA, Ireland
Department of Civil, Structural and Environmental Engineering, School of Engineering, Trinity College Dublin, College Green, Dublin, D02 PN40, Ireland
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
A.A.: Conceptualization (lead); Data curation (lead); Formal analysis (lead); Investigation (lead); Methodology (lead); Writing—original draft (lead); Writing—review and editing (lead). B.W., D.M., D.C., A.M., D.C., C.M.S., S.J.M., K.F.: Conceptualization (supporting); Investigation (supporting); Methodology (supporting); Writing—review and editing (supporting). I.S.: Project administration (lead); Resources (lead); Supervision (lead). All authors have given approval to the final version of the manuscript.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Ainabayev, A., Walls, B., Mullarkey, D. et al. High-performance p-type V2O3 films by spray pyrolysis for transparent conducting oxide applications. Sci Rep 14, 1928 (2024). https://doi.org/10.1038/s41598-024-52024-4
DOI: https://doi.org/10.1038/s41598-024-52024-4
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
540w Solar Module Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.